Sign In | Join Free | My spintoband.com
spintoband.com
Changzhou Junhe Technology Stock Co.,Ltd
Walk at the forefront of technology, to create a ceneration of famous brand!
Home > Zinc Flake Coating >

Low Friction Zinc Flake Coating / Zinc Nickel Plating Good Heat Resistance JH-9610

Changzhou Junhe Technology Stock Co.,Ltd
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment

Low Friction Zinc Flake Coating / Zinc Nickel Plating Good Heat Resistance JH-9610

Brand Name : JUNHE
Model Number : JH-9610
Certification : ISO9001 SGS
Place of Origin : Changzhou in china
MOQ : 100 Kiloamperes
Price : Negotiable
Payment Terms : L/C, T/T
Supply Ability : 2 Ton/Tons per Day
Delivery Time : Ten days after receipt of advance payment
Packaging Details : Pack A:20kg/ Metal Barrel Pack B:20KG Plastic Barrel Pack C:Based on the amount of B agent A
Color : Silver
Coating method : Dip and spray coating
PH(20℃) : 5.0-8.0
Specific gravity : 1.30-1.40 (spray coating )
Viscosity : According to operating demand
Operating temperature : 22±2℃
Contact Now
Chrome free water base zinc flake coating paint Silver Color PH ( 20℃ ) 5.0 - 8.0
Product Description

JH-9610is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.
Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.


Performance Charcteristic:

1. Chrome free
2. Good surface finish performance,high anti-corrosion,low friction coefficient.
3. No hydrogen brittleness,no pickling process.
4. Good heat resistance.
5. Good SST hours ,anti-aging cycle is long, can coat more products under the same process conditions.

Coating Process:

1. Mix Ratio
Pack A: Pack B: Pack C=1:1: X(according to different viscosity demand )

2. Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.

3. Add B to the stirring A slowly.

4. Stir the mixture about 1~2 hours after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 20℃, otherwise C will not be dissolved sufficiently .)Then stir 10~12 hours alowly and continuously.


Technical data:

No.ItemData
1ColorSilver
2Coating methodDip and spraying
3PH4.8-7.5
4Specific gravity1.45±0.1(Spray Coating)
5Viscosity25~40s(Spray Coating)



Mix Diagram:



Caution: Temperature should be controlled in above operation.


Coating Process:




Attentions:

1. Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.

2. Avoid irradiation of sunshine and ultraviolet ray for long time when operating, otherwise it will accelerate aging or polymerization of the coating .

3. It is very important to control the temperature of coating. If the temperature of coating changes when operating, it will effect the viscosity, then effec the coating quatity on workpiece. So the relations among temperature,viscosity and spinning process shoud be controlled well when coating.

4. The viscosity will be different if coating method is different. Choose low data if spray coating,and choose high data if dip spin coating.

























































Product Tags:

Anti Corrosion Coating

      

Mechanical Zinc Plating

      
China Customized Inflatable Bumper Ball Game Bubble Adult Grass CE supplier

Low Friction Zinc Flake Coating / Zinc Nickel Plating Good Heat Resistance JH-9610 Images

Inquiry Cart 0
Send your message to this supplier
 
From:
Enter your email please.
To: Changzhou Junhe Technology Stock Co.,Ltd
Subject:
Message:
Characters Remaining: (0/3000)
 
Inquiry Cart 0